TYPICAL HANDLING PROPERTIES 

Mix ratio by weight, (Resin/Hardener)  100/30 
Mixed Viscosity at 25℃ , cp  500-1000 
Pot Life at 25℃  (200 grams), hrs  >8 
Recommended Cure 2 hr @ 100℃ or 20 min @ 150℃
Alternate Cure 30 min/65℃+1 hr/150℃ 

TYPICAL CURED PROPERTIES 

Color Clear  Clear 
Specific Gravity  1.12
Hardness, Shore D  91
Water Absorption (24 hr @ 25℃ ), % 0.12  0.12
Lap Shear Strength to Aluminum, psi 2100  2100
Flexural Strength (yield), psi  19,500
Flexural Modulus (yield), psi 3.4x105
Service Temperature  -55℃ to 150℃
Glass Transition Temperature, ℃ 130  130
Coefficient of Linear Thermal Expansion, 10-6/℃  From -55℃ to 25℃  52
Dielectric Strength, Volts/mil  430
Dielectric Constant, 1 kHz  3.8
Dissipation Factor, 1 kHz Volume Resistivity, ohm-cm  0.01
Volume Resistivity, ohm-cm 2x1016