Property |
Test Method |
Unit |
Typical Value |
||
|
|
|
|
CATALYST 9 |
CATALYST 24 LV |
CATALYST 11 |
|
Hardness |
ASTM-D-2240 |
Shore D |
96 |
94 |
96 |
|
Flexural Strength |
ASTM-D-790 |
MPa |
104 |
103 |
123 |
|
Compressive Strength |
ASTM-D-695 |
MPa |
164 |
110 |
187 |
|
Linear Shrinkage |
ASTM-D-2566 |
cm/cm |
0,004 |
0,004 |
0,005 |
|
Water Absorption (24 hours) |
ASTM-D-570 |
% |
0,01 |
0,05 |
0,03 |
|
Coefficient of Thermal |
ASTM-D-3386 |
|
|
|
|
|
Expansion |
쁄1 쁄2 |
10-6/°C 10-6/°C |
29,7 96,0 |
31,9 93,0 |
27,4 87,3 |
|
Glass Transition Temperature |
ASTM-D-3418 |
°C |
77 |
47 |
111 |
|
Thermal Conductivity |
ASTM-D-2214 |
W/m.K |
1,36 |
1,12 |
1,31 |
|
Temperature Range of Use |
|
°C |
-40 to +130 |
-65 to +105 |
-55 to +155 |
|
Outgassing (1) |
ASTM-D-595 |
|
|
|
|
|
|
TML |
% |
0,33 |
- |
- |
|
|
CVCM |
% |
0,00 |
- |
- |
|
Dielectric Strength |
ASTM-D-149 |
kV/mm |
15,3 |
15,0 |
14,6 |
|
Dielectric @ 1 MHz |
ASTM-D-150 |
|
5,21 |
5,41 |
5,41 |
|
Dissipation Factor @ 1 MHz |
ASTM-D-150 |
|
0,036 |
0,059 |
0,047 |
|
Volume Resistivity @ 25°C |
ASTM-D-257 |
Ohm.cm |
1015 minium |
1015 minium |
1015 minimum |
(1) Outgassing : per NASA Reference Publication 1124. Sample tested was cured for 7 days at 25°C.